@MastersThesis{Yassuda:2006:EsCoRe,
author = "Yassuda, Irineu dos Santos",
title = "Estudo do comportamento de revestimentos superficiais em elementos
roscados de fixa{\c{c}}{\~a}o quando submetidos a torque",
school = "Instituto Nacional de Pesquisas Espaciais (INPE)",
year = "2006",
address = "S{\~a}o Jos{\'e} dos Campos",
month = "2006-02-23",
keywords = "parafusos, porcas, superf{\'{\i}}cies, corros{\~a}o, dacromet,
bicromatizados, fosfato, camada de zinco, bolts, nults, surfaces,
dacromet, dichromates, phosphate, zinc coating.",
abstract = "Neste trabalho, prop{\~o}e-se o estudo do efeito dos tratamentos
superficiais sobre o comportamento mec{\^a}nico de elementos
roscados, utilizados em ve{\'{\i}}culos automotivos comerciais.
Essa an{\'a}lise baseia-se na compara{\c{c}}{\~a}o das
superf{\'{\i}}cies resultantes nos revestimentos e nos
substratos destes elementos ap{\'o}s a aplica{\c{c}}{\~a}o de
diferentes esfor{\c{c}}os de torque e velocidade. Esses
esfor{\c{c}}os aplicados em condi{\c{c}}{\~o}es bastante
pr{\'o}ximas {\`a}s encontradas no processo produtivo normal,
mas com temperatura, torque e velocidades controlados. Esse tipo
de ensaio tornou-se poss{\'{\i}}vel gra{\c{c}}as ao advento das
parafusadora de torque e velocidades controladas por sistemas
digitais. Os resultados foram analisados por meio de microscopia
{\'o}ptica, para se determinar as condi{\c{c}}{\~o}es limites
do processo. Estas condi{\c{c}}{\~o}es s{\~a}o repetidas nos
ensaios que produziam amostras analisadas por microscopia
eletr{\^o}nica de varredura (MEV) e por espectroscopia por
energia dispersiva de raios X (EDX). Como existe uma extensa
variedade de elementos de fixa{\c{c}}{\~a}o roscados e de
revestimentos foram selecionados elementos M6 e M10 classe 8.8 com
os revestimentos mais comumente utilizados que s{\~a}o o
dacromet, bicromatizado, zinco negro e fosfatizado. A an{\'a}lise
desenvolvida pode ser utilizada como metodologia para a
determina{\c{c}}{\~a}o de par{\^a}metros de desenvolvimento de
processos de uni{\~o}es por elementos roscados. Esses
par{\^a}metros auxiliam a estabelecer a velocidade de montagem
que permita a conserva{\c{c}}{\~a}o dos tratamentos superficiais
dos parafusos e a otimiza{\c{c}}{\~a}o dos tempos de montagem,
permitindo, desta forma, maior produtividade, garantindo a vida
{\'u}til e a preserva{\c{c}}{\~a}o dos equipamentos. Os
resultados apresentam como as camadas dos revestimentos se
comportaram em termo de desgaste e os seus modos de falha.
Constata-se, tamb{\'e}m, que a falha da superf{\'{\i}}cie
est{\'a} mais relacionada {\`a} velocidade do processo e a falha
de substrato est{\'a} correlacionada ao torque aplicado.
ABSTRACT: The objective in this study is evaluation of mechanical
behavior of different types of superficial treatments in screw
threads used in commercial vehicles. This analysis was based on
the comparison of the resultant over surfaces of these elements
the application after different efforts of torques and speed.
These efforts had been applied in same conditions to ones normal
productive processes conditions, but with controlled temperature,
torque and speeds. This kind of test was possible after the advent
of equipments with torque and speeds controlled for digital
systems. The results had been analyzed by means of microscopy
optics to determine the conditions limits of the process and these
conditions had been repeated in validated samples had been
analyzed by scanning electronic microscopy (SEM) and Energy
Dispersive Spectrometry (EDS). There exists an extensive number of
different elements of setting and coatings had been selected M6
and M10 elements class 8.8 with coatings more used than are
dacromet, dichromate, black zinc and phosphate. The developed
analysis can be used as a methodology for the determination of
critical parameters of development of processes of unions for this
kind of elements, establish the optimum assembly speed to the
conservation of the superficial treatments of the screws reduction
of times of assembly, greater productivity, guaranteeing the
useful life and the preservation of the equipment. The results had
shown the failure mode of the layers and the interrelations speed
and layer consuming. It was also consisted that the failure of the
surface is related to the speed of the process and the substratum
failure is correlated to the applied torque.",
committee = "An, Chen Ying (presidente) and Piorino Neto, Francisco
(orientador) and Nono, Maria do Carmo de Andrade (orientadora) and
Dur{\~a}o, Ot{\'a}vio Santos Cupertino and Moura Neto, Carlos
de",
copyholder = "SID/SCD",
englishtitle = "Analysis of superficial covering behavior in screw threads of
fixture elements when submitted to torque",
language = "pt",
pages = "101",